92 %≤ | Al2O3+ Cr2O3 | Chemical composition |
3.1 ≤ | 1550℃×3h | B.D.(g/cm3) |
23≤ | 1550℃×3h | Modulus of rupture(Mpa) |
105≤ | 1550℃×3h | C.C.S(Mpa) |
![ول بلوک پاتیل](https://www.tamingar.com/wp-content/uploads/2017/10/ladle-well-block.jpg)
92 %≤ | Al2O3+ Cr2O3 | Chemical composition |
3.1 ≤ | 1550℃×3h | B.D.(g/cm3) |
23≤ | 1550℃×3h | Modulus of rupture(Mpa) |
105≤ | 1550℃×3h | C.C.S(Mpa) |